系统研究了不同品种的硅烷对不同配合比的海工混凝土防腐蚀性能的影响,探讨了龄期、养护条件、硅烷浓度、涂覆量、酸碱环境等因素对硅烷浸渍混凝土的防腐蚀性能的影响规律。试验结果表明,对不同配合比的海工高性能混凝土,试验所采用的硅烷使得其吸水率显著下降,氯离子吸收量的降低值也均大于90%,渗透深度达到3mm左右。说明,经硅烷浸渍的海工混凝土具有良好的耐腐蚀、耐久性。
|
|
In this paper, effects of different types of silanes on anti-corrosion properties of marine concrete with different mix proportions are studied systematically. Effects of age, curing conditions, silane concentration, thickness of coating and acid or alkaline environment on anti-corrosion properties of concrete immersed with silanes are discussed. The results indicate that, for high-performance marine concrete with different mix proportions, silanes make water absorption of concrete decrease greatly, the absorption value of chloride ion was reduced by more than 90%, and the penetration depth was about 3 mm. It indicates that marine concrete immersed with silanes exhibits excellent anti-corrosion property and durability.
|
|
基金项目：
|
|
上海青年科技启明星计划资助项目(04qmx1428)
|
|
作者简介：
|
|
|
|
参考文献：
|
|
[1] 黄君哲,周欲晓.海工混凝土结构表面涂层暴露试验及应用效果[J].中国港湾建设,2002,(6):17-20,51.
[2] 李俊毅.论耐用100年以上海工混凝土的基本技术条件[J].水运工程,2002,(5):4-7.
[3] 赵平.浅议影响海工混凝土耐久性的因素[J].港口工程,1997,(4):11-16.
[4] 施惠生,王琼.海工高性能混凝土用复合胶凝材料的试验研究[J].水泥,2003,(9):1-5.
[5] 欧阳幼玲,陈迅捷.腐蚀环境中海工混凝土抗氯离子侵蚀性[J].水利水运工程学报,2003,(1):39-43.
[6] BuenfeldNR,ZhangJZ.ChlorideDiffusionthroughSurface-TreatedMortarSpecimens[J].CementandConcreteResearch,1998,28(5):665-674.
[7] IbrahimM,Al-GahtaniAS,MaslehuddinM,etc. Effectivenessofconcretesurfacetreatmentmaterialsinreducingchloride-inducedreinforcementcorrosion[J].ConstructionandBuildingMaterials,1997,11(4):443-451.
[8] 黄月文,刘伟区.水乳型有机硅系表面处理剂的性能[J].涂料技术与文摘,2003,24(1):30-31.
[9] 黄桂柏,党涛.硅烷封闭涂料用于建构筑物的维护[J].新型建筑材料,1998,(5):23-25.
[10] Nolané,BasheerPAM,LongAE.Effectsofthree durabilityenhancingproductsonsomephysicalpropertiesofnearsurfaceconcrete[J].ConstructionandBuildingMaterials,1995,9(5):267-272.
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|
|