养护龄期对混凝土抗冻性能的影响

作者：李晓明 李俊毅 陈韬 李波

单位：中交天津港湾工程研究院有限公司 中交天津港湾工程研究院有限公司 中交天津港湾工程研究院有限公司 中交天津港湾工程研究院有限公司 天津 300222 天津 300222 天津 300222 天津 300222

关键词：抗冻性  养护龄期  试验研究

分类号：TU528.064

出版年,卷(期):页码：2007,31(2):30-33

摘要：

通过C30和C40两种强度等级的基准抗冻混凝土和掺加掺合料的抗冻混凝土分别在养护龄期14d和28d开始冻融的试验研究,表明适当缩短养护龄期对混凝土的抗冻性能影响不大。建议允许14d养护龄期开始冻融试验,对缩短冻融试验周期意义重大。

Based on the experiments and studies of the reference frost-resistant concrete and the frost-resistant concrete added with admixtures, with the strength of both types of concrete graded C30 and C40 respectively, which were tested with freezing and thawing cycles begun when the concrete was 14 and 28 days old respectively, it is indicated that appropriate shortening of the curing period produces no much influence upon the frost resistance of concrete. It is therefore recommended that starting freezing and thawing tests when the concrete is 14 days old should be permitted, which will produce great significance for shortening the period of freeze-thaw testing of concrete.

基金项目：

2003-2005年中港一航局技术开发基金项目(0331-84-0212)

作者简介：

参考文献：

[1]刘玉山．混凝土抗冻试件成型养护条件的商榷[J]．低温建筑技术,1999,(3)． [2]王海滨译．混凝土的冻融试验[J]．建材通讯,1979,(7)． [3]国外抗冻混凝土耐久性规范及试验方法(下册)[R]．天津港湾工程研究所,1993． [4] GBJ82-85,普通混凝土长期性能和耐久性试验方法[S]． [5] JTJ270-98,水运工程混凝土试验规程[S]． [6] DL/T5150-2001,水工混凝土试验规程[S]． [7]黄孝蘅．硬化混凝土中气泡性质对抗冻性影响的试验研究[J]．中国港湾建设,2003,(3)． [8]黄孝蘅．海工混凝土的抗冻性[R]．天津港湾工程研究所,1990． [9]阎培渝．用整体论方法分析混凝土的早期开裂及其对策[J]．建筑技术,2003,(1)． [10]洪定海．海港工程结构的材料科研成就与展望[A]．第四届全国海岸工程要求讨论会报告[C]．南京水利科学研究院,1986．

服务与反馈：

【文章下载】【加入收藏】