摘要：
|
|
本文概述了钢筋混凝土受弯构件腐蚀疲劳复杂的工作状态,分析了混凝土和钢筋材料的腐蚀疲劳破坏及其产生的原因,探讨了腐蚀疲劳钢筋混凝土受弯构件正截面验算方法的基本问题。针对破坏形态、极限状态、破坏准则等方面的问题提出了基本的观点,给出了确定的方法和原则。对腐蚀和疲劳共同作用造成的材料劣化,提出了量化的方法。修正了构件的几何参数,确定了混凝土边缘最大压应力和钢筋允许疲劳幅值的计算原则,给出了腐蚀疲劳的计算模式及其相关的参数计算方法。
|
|
This paper summarizes the complex service state, the failure reason of corrosion fatigue of concrete and reinforcement and the basic problem about flexural checking calculation of corrosion fatigue of reinforced concrete members Some problems such as failure mode, limit state, failure criterion are discussed and the corresponding determined principle is given A qualified means of material deterioration due to combined action of corrosion and fatigue and the modified geometric parameters of members are presented The calculation principle about the maximum compression stress of concrete and allowable fatigue ratio of reinforcement bar is given while a calculation mode for corrosion fatigue of flexural members and the calculation method for the relative parameters are presented
|
|
基金项目：
|
|
国家自然科学基金项目(50078009);;
辽宁省科学技术基金项目(001077)
|
|
作者简介：
|
|
|
|
参考文献：
|
|
[1] 袁迎曙,贾福萍,蔡跃.锈蚀钢筋的力学性能退化研究[J].工业建筑,2000,(1):43-46.
[2] 袁迎曙,贾福萍,蔡跃.锈蚀钢筋混凝土梁的结构性能退化模型[J].土木工程学报,2001,(3):47-52.
[3] 混凝土结构疲劳专题组.混凝土受弯构件疲劳可靠性验算方法的研究[A].中国建设科学研究院主编.钢筋混凝土研 究报告选集(3)[C].北京:中国建筑工业出版社,1994.
[4] 保荣,郭公玉,马士德等著.海洋腐蚀环境理论及其应用[M].北京:科学出版社,1999,132-142.
[5] RadianTalalAbdulmalek.effectofcorrosion,freeze-thawcycles,andtheircombinedeffectsonfatiguebehaviorofreinforcedconcrete[D].UniversityofRhodeIsland,1989
[6] GB5001-2002,混凝土结构设计规范[S].
[7] 沈海军,李国志.腐蚀疲劳裂纹扩展过程中裂纹尖阳极溶解的贡献[J].西北工业大学学报,2001,(2):225-228.
[8] 王荣,郑修麟.加载频率和超载对腐蚀疲劳裂纹起始寿命的影响[J].中国腐蚀与防护学报,1996,(6):256-262.
[9] 李志义,丁信伟.金属材料的腐蚀疲劳[J].化工机械,1995,(4):53-56.
[10] 牛荻涛.海洋环境下混凝土强度的经时变化模型[J].西安建筑科技大学学报,1995,(1):49-52.
[11] 太原工学院土木系.钢筋混凝土受弯构件正截面疲劳验算方法的研究[A].中国建筑科学研究院主编.钢筋混凝土研究报告选集(2)[C].北京:中国建筑工业出版社,1981.9
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|
|